Descrizione
Santa Barbara High Translucent White Zirconia is the high strength, high translucency monolayer solution that allows you to obtain excellent results with a natural effect. It is supplied in white and allows it to be colored according to needs, guaranteeing multiple operational solutions. The other flexural strength (1350 Mpa) allows long-lasting and safe restorations suitable for any type of processing.
Compatible with the entire Santa Barbara Dental fleet
* • White color
* • Flexural Strength 1350Mpa
* • Translucency 37%
* • Natural effect
* • Lightweight and durable
* • Biocompatible
* • Low thermal conductivity
* • Ideal for crowns, bridges and veneers
Chemical composition
Components
ZrO2 + HfO2 + Y2O3 ≥99%
Y2O3 4.5% -6.0%
Al2O3 <0.25%
Other Oxides <0.15%
Physical characteristics
Property
Density before sintering (gcm − 3)
3.15 ± 0.05
Density after sintering (gcm − 3)
6.09 ± 0.01
CTE (25-500 ° C) 10.5 ± 0.05
Flexural strength after sintering (Mpa) 1350
Surface monoclinic phase content of accelerated aging <15%
Light transmittance 37%
Chemical Solubility after sintering (µg · cm − 2) & lt; 100
Cytotoxicity Level 0
Radioactivity (Bq g − 1) & lt; 0.1
Sintering temperature 1500 -1550
Dimensions
Diameter (mm) Thickness (mm)
98 10
98 12
98 14
98 16
98 18
98 20
98 22
98 25
Informazioni Aggiuntive
| Weight | 480 g |
|---|---|
| Misure Cialde | ∅98×10, ∅98×12, ∅98×14, ∅98×16, ∅98×18, ∅98×20, ∅98×25 |
| Colore Cialda | A1, A2, A3, A3,5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4 |