Description
Santa Barbara Dental
Super Translucent White Zirconia
is the high-strength, high-translucency monolayer solution for excellent natural-looking results. It is supplied in white and can be colored as required, providing a variety of operative solutions. The high flexural strength (1200 MPa) enables safe and durable restorations suitable for all types of processing.
Compatible with the entire Santa Barbara Dental fleet
• Color: White
• Flexural Strength 1200Mpa
• Translucency 43%
• Natural tooth looking
• Lightweight and durable
• Biocompatible
• Low thermal conductivity
• Suitable for crowns and posterior bridges
Chemical Composition
| Components | |
|---|---|
| ZrO2+HfO2+Y2O3 | ≥99% |
| Y2O3 | 4.5%-6.0% |
| Al2O3 | <0.15% |
| Altri ossidi | <0.15% |
Physical Properties
| Properties | |
|---|---|
| Density before sintering (g·cm−3) | 3.15 ±0.05 |
| Density after sintering (g·cm−3) | 6.09 ±0.01 |
| CTE (25-500°C) | 10.5 ±0.05 |
| Flexural strength after sintering (Mpa) | 1200 |
| Aging surface monoclinic phase content | <15% |
| Light Transmittance | 43% |
| Chemical solubility after sintering (µg·cm−2) | <100 |
| Cytotoxicity | Livello 0 |
| Radioactivity (Bq·g−1) | <0.1 |
| Sintering Temperature | (recommended 1530) 1500 -1550 |
More information
| Weight | 350 g |
|---|---|
| Misure Cialde | ∅98×10, ∅98×12, ∅98×14, ∅98×16, ∅98×18, ∅98×20, ∅98×25, ∅98×22 |